A-A12O3 nanopowders were prepared by sol-gel method using industrial alumina sol as raw material. To study the effects of gel conditions, seed addition, mineralizer type and addition amount, calcination temperature and holding time on the product. The results show that the smaller the particle size after sol degumming, the smaller the particle size of the product, the lower the calcination temperature required to obtain the product; the introduction of seed crystals and mineralizer can promote the conversion of transition alumina to a-A12O3. The phase transition temperature is lowered; the calcination temperature has a great influence on the formation of aA12O3. When the temperature is constant, the prolonged holding time has little effect on the product phase. The optimum conditions for preparing a-A12O3 nanopowder by sol-gel method are: the dispersant triethanolamine is used in an amount of 1% (mass fraction), the seed crystal is added in 5%, the NH4NO3 is added in 5%, and the calcination temperature is 1000oC. The holding time is 2 h. The obtained a-A12O3 nano-powder has a spherical appearance, uniform particle size distribution and a particle size of about 50 nm. (Diamond and Abrasives Engineering, 2009, Issue 1)
Self-tapping threaded inserts are suitable for creating heavy-duty, wear-resistant and vibration-proof fastenings in materials with low shear strength, such as aluminium, brass, bronze, cast iron or duro and thermoplastics. Threaded inserts with cutting slot are available in steel and stainless-steel versions.
Self Tapping Insert,302 Self-Tapping Insert,Self Tapping Insert Type 302,Thread Inserts Type Of 307 Steel